Nickel 201 Ring Bar
Nickel 201 Ring Bar | Nickel 201 Circle/Ring Bar Supplier in India | Nickel 201 Ring Bar Price in India | Nickel 201 Ring Bar Properties
Trusted Nickel 201 Ring Bar supplier and dealer of Durable and Corrosion-Resistant products
Nickel 201 Ring Bar is produced from commercially pure wrought nickel with a minimum nickel content of 99.6% and a controlled low carbon composition. This low carbon level makes Nickel 201 especially suitable for high-temperature applications, as it offers superior resistance to intergranular embrittlement when exposed to temperatures above 315°C.
Which industries do we cater to as a Nickel 201 Circle/Ring Bar supplier and dealer?
There are several industries that require high purity nickel, having excellent corrosion resistance. Hence we at Nickel Alloy Corporation a Top Nickel 201 Circle/Ring Bar in India present the following industries given below Premium Quality Nickel 201 Circle/Ring Bar.
- Petrochemical & Oil Refineries
- Chemical Processing Industry
- Power Generation
- Electronics & Electrical Industry
- Food Processing Industry
- Aerospace & Defense
- Pharmaceutical Industry
Specifications Table of Nickel 201 Ring Bar
| Parameter | Specification |
|---|---|
| Material Grade | Nickel 201 |
| UNS Number | N02201 |
| ASTM Standards | ASTM B160, ASTM B564 |
| Product Form | Circle Bar / Ring Bar |
| Manufacturing Process | Hot Rolled, Forged, Machined |
| Outer Diameter (OD) | 100 mm – 2000 mm |
| Inner Diameter (ID) | 50 mm – 1800 mm |
| Thickness / Height | 10 mm – 500 mm |
| Length | As per drawing / requirement |
| Surface Finish | Black, Bright, Machined, Polished |
| Condition | Annealed |
| Density | 8.89 g/cm³ |
| Melting Point | 1446 °C |
| Heat Treatment | Annealed |
| Tolerance | As per ASTM / Customer Specification |
| Testing | Chemical, Mechanical, PMI, Ultrasonic |
| Certification | Mill Test Certificate (EN 10204 3.1) |
| Applications | Heat Exchangers, Chemical Processing, Aerospace, Marine, Power Plants |
Physical Properties & Characteristics of Nickel 201 Ring Bar
| Property | Value |
|---|---|
| Density | 8.89 g/cm³ |
| Melting Point | 1446 °C |
| Thermal Conductivity | 67 W/m·K |
| Electrical Resistivity | 0.096 µΩ·m |
| Coefficient of Thermal Expansion | 13.3 µm/m·°C |
| Specific Heat Capacity | 456 J/kg·K |
| Modulus of Elasticity | 207 GPa |
| Magnetic Permeability | Ferromagnetic |
| Poisson’s Ratio | 0.31 |
| Hardness | 70 – 90 HRB |
| Corrosion Resistance | Excellent in caustic alkalis |
| Oxidation Resistance | Good up to elevated temperatures |
| Weldability | Excellent |
| Formability | Excellent |
| Machinability | Good |
Chemical Composition of Nickel 201 Ring Bars
| Element | Composition (% by Weight) |
|---|---|
| Carbon (C) | 0.004 |
| Silicon (Si) | 0.03 |
| Manganese (Mn) | 0.14 |
| Phosphorus (P) | < 0.005 |
| Sulfur (S) | < 0.0010 |
| Cobalt (Co) | < 0.01 |
| Nickel (Ni) | ≥ 99.61 |
| Copper (Cu) | ≤ 0.01 |
| Magnesium (Mg) | < 0.005 |
| Iron (Fe) | < 0.01 |
Mechanical Properties of Nickel 201 Ring Bars
| Property | Value |
|---|---|
| Tensile Strength | 380 MPa min |
| Yield Strength (0.2% Offset) | 103 MPa min |
| Elongation | 40% min |
| Hardness | 70 – 90 HRB |
| Modulus of Elasticity | 207 GPa |
| Impact Strength | Good |
| Fatigue Resistance | Good |
| Creep Resistance | Good at elevated temperatures |
| Ductility | Excellent |
| Toughness | Excellent |
Equivalent Grade of Nickel 201 Ring Bars
| Standard | Equivalent Grade |
|---|---|
| UNS | N02201 |
| ASTM | Nickel 201 |
| DIN | 2.4061 |
| EN | Ni 99.5 |
| ISO | Ni 99.5 |
| JIS | NW 2201 |
| BS | NA 12 |
Nickel 201 Ring Bars Size Chart
| Outer Diameter (OD) | Inner Diameter (ID) | Thickness / Height |
|---|---|---|
| 100 mm | 50 mm | 10 mm |
| 150 mm | 75 mm | 15 mm |
| 200 mm | 100 mm | 20 mm |
| 300 mm | 150 mm | 25 mm |
| 400 mm | 200 mm | 30 mm |
| 500 mm | 250 mm | 40 mm |
| 600 mm | 300 mm | 50 mm |
| 800 mm | 400 mm | 60 mm |
| 1000 mm | 500 mm | 80 mm |
| 1200 mm | 600 mm | 100 mm |
| 1500 mm | 750 mm | 150 mm |
| 2000 mm | 1000 mm | 200 mm |
Why is Nickel Alloy Corporation a distinguished Nickel 201 Ring Bar supplier?
There are few reasons why we Nickel Alloy Corporation is one of the Best Nickel 201 Circle/Ring Bar Manufacturer in India. They are given below:
Strict Quality Control & Testing
Every Nickel 201 ring and circle bar undergoes rigorous quality inspections, including chemical composition analysis, mechanical testing, dimensional checks, and surface finish inspection to meet international standards.Wide Size Range & Customization
Nickel Alloy Corporation offers standard and customized sizes, thicknesses, and diameters of Nickel 201 circle and ring bars, tailored to meet specific project and machining requirementsCompliance with International Standards
Our products conform to ASTM, ASME, DIN, and EN specifications, ensuring global acceptance across chemical, petrochemical, power, and engineering industries.Advanced Manufacturing & Finishing
Using modern cutting, forging, and machining techniques, we deliver Nickel 201 rings with precise tolerances, uniform grain structure, and superior surface finish, ideal for critical applications.Strong Supply Chain & On-Time Delivery
With a well-managed inventory and logistics network, we ensure prompt deliveries, minimizing downtime and supporting tight project schedules.Competitive Pricing
By maintaining efficient sourcing and production processes, we deliver cost-effective Nickel 201 circle and ring bars without compromising on quality.
Connect with us today to support your operations with precision and unmatched excellence.